Task „Implementation of procedures ensuring the originality of scientific papers published in the quarterly „Eksploatacja i Niezawodność – Maintenance and Reliability” financed under contract 532/P-DUN/2018 from the funds of the Minister of Science and Higher Education for science dissemination activities.
Gas nitriding of precipitation-hardening stainless steels
Azotowanie gazowe stali nierdzewnych utwardzanych wydzieleniowo
In this paper investigation results of nitrided layers on 17-4PH stainless steel have been presented. Addition of ammonia chloride to nitriding atmosphere was applied as activation method. Microhardness of created layers reaches 1300 HV. Plastic properties were also satisfactory. Both hardness and thickness depend on nitriding temperature. Optimum temperature range of thermo - chemical treatment was determined Influence of precipitate processes taking place during heat treatment on nitriding kinetics and layer properties was proved.
Poddano azotowaniu gazowemu nierdzewną stal utwardzaną wydzieleniowo 17-4PH. Jako metodę aktywacji zastosowano dodatek do atmosfery chlorowodoru, będącego produktem dysocjacji chlorku amonowego. Wytworzone warstwy charakteryzowały się wysoką twardością, niewielką kruchością, przy czym zarówno twardość jak i grubość warstwy są funkcją temperatury azotowania. Określono optymalny zakres temperatur obróbki cieplno - chemicznej. Potwierdzono wpływ zachodzących podczas obróbki cieplnej procesów wydzieleniowych na przebieg azotowania oraz na strukturę i właściwości wytwarzanych warstw.
41-44